KAOLIN
| NATURE | KAOLIN * | |||
|---|---|---|---|---|
| TRADE NAME | SFB | MS | MPO | ASC |
| DRY FLEXURAL STRENGTH (Kgf/cm2) | 48 | ≥ 11 | ≥ 14 | 114 |
| FIRED FLEXURAL STRENGTH (Kgf/cm2) | 401 | 280 | 320 | 540 |
| FIRING TEMPERATURE | 1015 ºC | 1150 ºC | 1150 ºC | 1068 ºC |
| CHEMICAL COMPOSITION 2 (%) | ||||
| SiO2 | 52,2 | 53,2 | 53,2 | 56,1 |
| AI2O3 | 31,85 | 32,75 | 32,50 | 21,21 |
| Fe2O3 | 0,67 | 0,60 ± 1,10 | 0,90 ± 0,10 | 3,44 |
| CaO | 0,20 | 0,05 | 0,05 | 0,20 |
| MgO | 0,03 | 0,18 | 0,21 | 7,56 |
| Na2O | 0,19 | 0,05 | 0,06 | 0,49 |
| K2O | 0,41 | 1,80 ± 0,10 | 1,90 ± 0,10 | 2,35 |
| TiO2 | 0,19 | 0,25 ± 0,10 | 0,40 ± 0,10 | 0,47 |
| P2O5 | - | 0,04 | 0,05 | 0,11 |
| MnO | 0,005 | - | - | - |
| P.R. / L.O.I (limiting oxygen index) | 12,7 | 10,6 | 10,4 | 7,6 |
| 2 F.R.X. | ||||
| HUMIDITY | ≤ 20% | ≤ 20% | ≤ 20% | ≤ 20% |
*The production of this product is based on natural raw materials, therefore we reserve the right to modify the values presented.